光伏鍍膜玻璃
玻璃厚度∶ 1.6mm-3.2mm
常規(guī)厚度∶1.6mm/1.8mm/2.0mm/2.5mm/3.2mm
最大尺寸∶1350*2600mm
透光率∶ （3.2mm）≥93.5%
附著力∶ 用百格力
膜層硬度∶ ≥3 H
耐堿性∶在60℃過飽和的堿液中浸泡24小時后，透光率平均值衰減0.20%
耐酸性∶在2℃高濃度鹽酸中浸泡24小時后，透光率平均值衰減0.20%
耐鹽霧腐蝕性∶在鹽霧試驗(yàn)機(jī)種放置96小時后，膜層無起泡，無剝落，無明顯變色，透光率平均值衰減0.60%
耐恒溫恒濕性∶在恒溫恒濕箱中以溫度85℃，溫度85%的條件下放置100小時后，透光率平均值衰減0.50%
AR-Coating solar glass
Thickness: 1.6mm-3.2mm
Common Thickness:1.6mm/1.8mm/2.0mm/2.5mm/3.2mm
Max-size: 1350*2600mm
Transmittance: (3.2mm)≥93.5%
Adhesion: With Cross-Cut Tester
Film Hardness: ≥3H
Alkali Resistant: At 60℃ soaked saturated solution after 24 hours,the average transmittance attenuation 0.20%.
Acid Resistant: Soak 24 hours at25℃ high concentration of hydrochloric acid,light transmittance of 0.20% average attenuation.
Salt Spray: Placed for 96 hours in a salt spray test machine,film no blisters,no peeling off,no color,light transmittance of 0.60% average attenuation.
High Temperature&Humidity: In constant temperature and humidity box in the temperature of 85℃,85% humidity conditions for 1000 hours the average transmittance attenuation 0.50%.
玻璃厚度∶ 1.6mm-3.2mm
常規(guī)厚度∶1.6mm/1.8mm/2.0mm/2.5mm/3.2mm
最大尺寸∶1350*2600mm
透光率∶ （3.2mm）≥93.5%
附著力∶ 用百格力
膜層硬度∶ ≥3 H
耐堿性∶在60℃過飽和的堿液中浸泡24小時后，透光率平均值衰減0.20%
耐酸性∶在2℃高濃度鹽酸中浸泡24小時后，透光率平均值衰減0.20%
耐鹽霧腐蝕性∶在鹽霧試驗(yàn)機(jī)種放置96小時后，膜層無起泡，無剝落，無明顯變色，透光率平均值衰減0.60%
耐恒溫恒濕性∶在恒溫恒濕箱中以溫度85℃，溫度85%的條件下放置100小時后，透光率平均值衰減0.50%
AR-Coating solar glass
Thickness: 1.6mm-3.2mm
Common Thickness:1.6mm/1.8mm/2.0mm/2.5mm/3.2mm
Max-size: 1350*2600mm
Transmittance: (3.2mm)≥93.5%
Adhesion: With Cross-Cut Tester
Film Hardness: ≥3H
Alkali Resistant: At 60℃ soaked saturated solution after 24 hours,the average transmittance attenuation 0.20%.
Acid Resistant: Soak 24 hours at25℃ high concentration of hydrochloric acid,light transmittance of 0.20% average attenuation.
Salt Spray: Placed for 96 hours in a salt spray test machine,film no blisters,no peeling off,no color,light transmittance of 0.60% average attenuation.
High Temperature&Humidity: In constant temperature and humidity box in the temperature of 85℃,85% humidity conditions for 1000 hours the average transmittance attenuation 0.50%.